REINFORCEMENT FIBER

Basalt Fiber Sheet

150 mm wide × 50 m roll | 310 g/m²

Basic information

Dimensions: 150 mm × 50 m roll
Areal weight: 310 g/m²
Material category: Inorganic fiber

Sales specification: 150 mm × 50 m roll, 310 g/m².

Documents

Documents are provided as original Japanese-language PDFs. Each card includes a concise English summary for orientation.

2022 tensile-strength test report No. 22A2534

2022 Japanese test report for tensile-strength testing of four basalt-fiber resin-impregnated sheet specimens; the report records an average tensile strength of 2100 MPa under its stated conditions.

PDF / Japanese

↗

Basalt material test report No. 200932185

2009 material test report listing tensile strength, elastic modulus, elongation, flexural strength, interlaminar shear strength and concrete-composite bond results for the tested basalt material.

PDF / Japanese

↗

2011 continuous-footing fiber-reinforcement experiment

2011 Japanese experimental report comparing continuous-footing specimens with and without basalt or aramid fiber-sheet reinforcement under the described loading program.

PDF / Japanese

↗

Comparison of basalt and other fibers

One-page Japanese reference table comparing general material-property data for basalt, carbon and aramid fibers; it is reference data rather than the current product guarantee specification.

PDF / Japanese

↗

Notes on basalt test data

Japanese technical note explaining how raw-fiber test values differ from sheet-product performance and cautioning users not to treat the raw-fiber values as equivalent to the finished sheet.

PDF / Japanese

↗

TEST DATA

Basalt Sheet Test Data

Test values are results under the conditions stated in each report and are not guaranteed product values.

2022 | Japan Testing Center for Construction Materials

Tensile Test of Basalt-Fiber Reinforced Resin Sheets

Four resin-impregnated sheets submitted by Fiberdine were tested at 2 mm/min. The average tensile strength in Report No. 22A2534 was 2100 MPa (2.10 kN/mm²).

No. 1: 2300 MPa
No. 2: 2130 MPa
No. 3: 1880 MPa
No. 4: 2080 MPa
Average: 2100 MPa

Submitted test conditions: design thickness 0.12 mm, full sheet width 150 mm and 68 fiber bundles across the full width. Test specimens comprised basalt fiber, nylon weft and epoxy resin.

View test report · PDF / Japanese ↗

2009 tensile strength2.303 kN/mm²2303 MPa

2009 tensile modulus10.5 kN/mm²1.05×10⁴ MPa

2009 elongation2.18%GB/T3354-1999

2009 flexural strength299.8 MPaGB/T3356-1999

2009 interlaminar shear strength29.8 MPaGB5036-2006

2009 concrete-composite tensile strength4.28 MPaFailure within concrete

2009 Material Test Report No. 200932185 test specimen: 341 g/m².